EVA Film for Encapsulating Solar Module
UV aging resistance, Resistance to temperature&Moisture.easily operate.Good light transmittance, anti-aging,long-time bonding.
Lushan™ EVA film is suitable for encapsulating silicon module, thin film module and BIPV module, which uses resins of VA content 30%-33% as its main material, provided with properties of high transmission, strong adhesion and long term performance. Thickness is from 0.3-0.8mm, while width is within 2000mm.The finished solar module is the cured battery plate which goes through trimming, cleaning, and installing aluminum alloy frame, testing and then packing.
I. Product Series
EV10: Fast curing Series
II. Spercifications
1. Appearance: single light pattern.
2. Thickness: Providing 0.3 ~ 1.0mm thickness of the various products, 0.50mm thickness of conventional products.
3. Width: Any width below 1950mm; common width are: 350, 550, 670, 810, 820, 980, 1000 mm and so on.
4. Length of each roll: 0.50mm thickness of conventional products with the length of 100m.
Different thickness with different length. Large quantities can be discussed separately.
III. Basic Properties
Item | Unit | Technology Data | Typical Data |
Melt Index (after curing ) | g/10 mins | —— | 30 |
Softening Point (before curing) | °C | —— | 58 |
Density | g/cm³ | —— | 0.96 |
Apperance | Visual | smooth surface, uniform thickness, no discoloration, non-stick at room temperature | Pass |
Transparence (after curing) | % | ≥91.0(400-1100nm) | 91.5 |
UV- Cutoff Wavelength | Nm | —— | 360 |
Peeling Strength (140°C,15min after curing) | N/cm | ≥ 60 (glass/film) | 70 |
≥ 40 (TPT/film) | 48 | ||
Cross linking rate (140°C,15min) | % | 75-85 | 80 |
Shrinkage Rate (before curing, 120°C,3min) | % | ≤4% | 3% |
Tensile Strength (after curing) | MPa | ≥20 | 21.5 |
Elongation at Break (after curing) | % | ≥500 | 518 |
Water Absorption (25°C,24h) | % | ≤0.1 | 0.06 |
Humidity Resistance (85°C, 85%, 1000h) | No bubble, no peeling, no discoloration, power loss<5%, filmYI≤2 | Pass | |
Heat Resistance (100°C,2h) | No bubble, no peeling, no discoloration | Pass | |
UV-accelerating aging (280-385nm 15kwh/ m2) | No cracking, no discoloration, power loss<5%, filmYI≤2 | Pass | |
Artificially-accelerating aging (3000hour, Xenon light 63°C,65%) | No cracking, no discoloration, power loss<5%, filmYI≤2 | Pass | |
Resistance to temperature (from -40°C to 85°C,50cycles) | No bubble, no cracking, no peeling, no discoloration, no expansion with heat and contraction with cold, power loss<5%, filmYI≤2 | Pass | |
Resistance to Moisture and Cold (from -40°C to 85°C,85%,10cycles) | No bubble, no cracking, no peeling, no discoloration, no expansion with heat and contraction with cold, power loss<5%, filmYI≤2 | Pass |
IV. Processing Method
Type Operating condition | Fast curing type | |||
EV10 | ||||
Curing method | One-step method | Two-step method | ||
Laminated curing | Heating plate temperature(°C) | 135-140 | 145-150 | 120-130 |
Vaccuum time(min) | 5-8 | 4-6 | 4-6 | |
Pressing & maintaining time(min) | 12-20 | 6-12 | 4-8 | |
Oven curing | Temperature(°C) | —— | —— | 135-145 |
Time(min) | —— | —— | 15-20 |